Shin-Etsu's KE-3456 is a fast, single component, room-temperature curing conformal coating that will cure to form a durable and flexible elastomer for protecting electronic components. KE-3456 is suitable for application by selective spray coating, mass coating, and flow coating, making it ideal for coating circuit boards.
- Superior protection of sulfurization of substrate
- Fast cure
- Single component
- Room-temperature cure
- Low odor and non-corrosive
- Excellent unprimed adhesion to most substrates
- Coating circuit boards and other electronic components
- Protecting substrates from sulfur corrosion
Light Yellow Transparent
Density @ 23C (g/cm3)
7days @ 23C/50% RH
Tensile Strength (MPa)
Volume Resistivity (TΩ·m)
Dielectric Strength (kV/mm)
2.6 @ 50Hz
Dielectric Dissipation Factor
4.0 x 10-4 @ 50Hz
Usable Temperature Range (C)
-40 to +180
Note: Values are not for specification purposes.
Warranty- The information and data contained herein are believed to be accurate and reliable; however it is the user's responsibility to determine suitability of use.
Since Shin-Etsu Silicones, Inc. cannot know all of the uses to which its products may be put or the conditions of use, it makes no warranties concerning the fitness or suitability of its products for a particular use or purpose. You should thoroughly test any proposed use of our products and independently conclude satisfactory performance in your application. Likewise, if the manner in which our products are used requires governmental approval or clearance, you must obtain it. Shin-Etsu Silicones, Inc. warrants only that its products will meet its specifications. There is no warranty of merchantability of fitness of use, nor any other expressed or implied warranties. The user's exclusive remedy and Shin-Etsu Silicones, Inc.'s sole liability is limited to refund of the price or replacement of any product shown to be otherwise than as warranted. Shin-Etsu Silicones, Inc. will not be liable for incidental or consequential damages of any kind. Suggestions of uses should not be taken as inducements to infringe any patents.